Advanced Materials Research, Trans Tech Publications, Ltd., Vol. 895 ( 2014-2), p. 221-225
Abstract:
Poly(vinylidene flouride)/nano-magnesium oxide (PVDF/MgO) nanocomposites with MgO loading percentage of (7% wt. %) were annealed with various annealing temperatures ranging from 70°C to 170°C with rapid removal from the oven. From dielectric constant, the samples annealed at temperature of 70°C showed an improvement in the dielectric constant from 21 to 23 at frequency 10 3 Hz for UN and AN70 respectively. However, as the temperatures were increased, the dielectric constant of PVDF/MgO (7%) was found to decrease. XRD showed the presence of β-phase for PVDF/MgO(7%) sample annealed at 70°C in comparison to unannealed sample, hence PVDF/MgO(7%) film is suitable to be used for low frequency capacitor application.
Type of Medium:
Online Resource
ISSN:
1662-8985
DOI:
10.4028/www.scientific.net/AMR.895
DOI:
10.4028/www.scientific.net/AMR.895.221
Language:
Unknown
Publisher:
Trans Tech Publications, Ltd.
Publication Date:
2014
detail.hit.zdb_id:
2265002-7
Permalink