Advanced Materials Research, Trans Tech Publications, Ltd., Vol. 832 ( 2013-11), p. 718-723
Kurzfassung:
Poly (vinylideneflouride)/nanomagnesium oxide (PVDF/MgO) nanocomposites with MgO loading percentage of 7% were annealed with various annealing temperatures ranging from 70oC to 170oC. The PVDF/MgO(7%) thin films were fabricated using spin coating technique with MIM structure. The dielectric constant of PVDF/MgO(7%) was studied over a wide range of annealing temperatures with rapid removal from the oven once the annealing was utilized. The nanocomposites thin films annealed at temperature of 70oC (AN70) shows an improvement in the dielectric constant of 23 at 10 3 Hz compared to unannealed sample (UN), which was 21 at the same frequency. However, as the annealing temperatures were increased from 90oC (AN90) to 170o C (AN170), the dielectric constant of PVDF/MgO(7%) were found to decrease from 16 to 7 respectively, which were lower than the UN thin films. AN70 also produced low value of tangent loss at low frequency˼˰˸̱̈́̾˰δ˹˰̴̷̹̹̳̱̹̾̈́̾˰̸̱̈́̈́˼˰̵̷̱̱̼̹̾̾̾˰̱̈́˰temperatures 70oC is favourable temperature used to improve the dielectric constant of PVDF/MgO(7%).
Materialart:
Online-Ressource
ISSN:
1662-8985
DOI:
10.4028/www.scientific.net/AMR.832
DOI:
10.4028/www.scientific.net/AMR.832.718
Sprache:
Unbekannt
Verlag:
Trans Tech Publications, Ltd.
Publikationsdatum:
2013
ZDB Id:
2265002-7
Permalink