Tanzania Journal of Science, African Journals Online (AJOL), Vol. 47, No. 4 ( 2021-10-28), p. 1362-1375
Abstract:
Mesoporous carbon has been synthesized by activating carbonized biogas slurry residues with ZnCl2 and KOH simultaneously. The carbon to activating agent mass ratios were kept at 1:4, while the ZnCl2 to KOH mass ratio varied from 4:0, 3:1, 2:2, 1:3, to 0:4. The highest BET specific surface area of 361 m2 g-1, micropore surface area of 231 m2 g‒1, mesopore surface area of 125 m2 g‒1, and total pore volume of 0.23 cm3 g‒1 which amounted to 78% mesopore content, were obtained for the sample with 3:1 ZnCl2 to KOH mass ratio. Scanning electron microscope (SEM) images were acquired to determine the surface morphology and energy dispersive X-ray (EDX) was used to determine surface composition of the samples. The short, medium, and long-range orders of the synthesized materials were studied using pair distribution function (PDF) analysis. PDF showed that in addition to the locally ordered carbon and silica phase components, samples activated using combined ZnCl2 and KOH also contained crystalline Zn2SiO4 phase with the willemite structure. Electrochemical studies in three-electrode cell system revealed maximum specific capacitance of 216 F g‒1 exhibited by sample with a ZnCl2: KOH mass ratio of 3:1 at a scan rate of 5 mV s‒1. Keywords: Mesoporous carbon; Pair distribution function, Specific capacitance, supercapacitor
Type of Medium:
Online Resource
ISSN:
2507-7961
,
0856-1761
Language:
Unknown
Publisher:
African Journals Online (AJOL)
Publication Date:
2021
detail.hit.zdb_id:
2641763-7
SSG:
11