Key Engineering Materials, Trans Tech Publications, Ltd., Vol. 697 ( 2016-7), p. 44-48
Abstract:
Zirconium diboride (ZrB 2 ) powders with no impurities were prepared using zirconium oxide (ZrO 2 ), boron carbide (B 4 C) and carbon black as raw material by carbon thermal reduction. The phase composition of ZrB 2 powders was characterized by X-ray diffraction (XRD) and the micro-morphology was observed by scanning electron microscope (SEM). The effects of B4C content, calcination temperature and holding time were studied on the formation of ZrB2 powders. The results indicated that ZrB 2 powders could be successfully synthesized while holding for 1.5 h at 1600 °C in Ar atmosphere. When the content of B 4 C was 17.7 wt% , there existed the crystal phase of ZrB 2 only. The impurities could be easily led in with the increase of content of B 4 C. ZrB 2 powders with the size from 1-5 μm could be obtained eventually and the particle size grew obviously with increase of the holding time.
Type of Medium:
Online Resource
ISSN:
1662-9795
DOI:
10.4028/www.scientific.net/KEM.697
DOI:
10.4028/www.scientific.net/KEM.697.44
Language:
Unknown
Publisher:
Trans Tech Publications, Ltd.
Publication Date:
2016
detail.hit.zdb_id:
2073306-9