In:
Revista de Odontologia da UNESP, FapUNIFESP (SciELO), Vol. 46, No. 2 ( 2017-03-16), p. 116-123
Abstract:
Abstract Introducion The development of glass ionomer cements brought advantages to direct restorative procedures due to properties such as chemical adhesion to dental structure and fluoride release. Nevertheless, oral environment may provide conditions which can alter material surface. Objective To evaluate surface roughness and surface morphology of four glass ionomer cements (Ketac Molar Easy Mix, Vitremer, Vitro Molar e Maxxion) when immersing on different artificial saliva. Material and method Ten specimens of each material were fabricated and surface roughness was measured before and after immersion on neutral and acid artificial saliva for 28 days using a rugosimeter (Surftest SJ–40) and microscopy analysis by scanning electron microscopy. Roughness data were analyzed statistically by Kruskal-Wallis test, Wilcoxon test and Mann Whitney test, at 5% significance level. Result Roughness values were statistically higher after immersion on neutral and acid artificial saliva for all materials, except for Vitromolar that did not presented no statistical difference between roughness values before and after immersion on neutral saliva. The Maxxion R presented statistically higher roughness values compared to all materials after immersion on neutral and acid artificial saliva. Conclusion The superficial roughness of glass ionomer cement increased after immersion on neutral and acid artificial saliva for most of the materials. Acid storage solution promoted a greater increase in surface roughness after immersion of the specimens for Maxxion and Vitro Molar.
Type of Medium:
Online Resource
ISSN:
1807-2577
DOI:
10.1590/1807-2577.20716
Language:
Unknown
Publisher:
FapUNIFESP (SciELO)
Publication Date:
2017