Modern Physics Letters B, World Scientific Pub Co Pte Ltd, Vol. 23, No. 31n32 ( 2009-12-30), p. 3725-3729
Abstract:
The ferrite added with Bi - Zn - Al - B - Si - O nano-glass was sintered at 840-900°C, 2 h and the initial permeability, quality factor, density and saturation magnetization of the samples were measured. The initial permeability of the nano-glass added sample was about 62.6 at 0.1 wt%, and showed a sharp increase from 0.4 to 0.5 wt%. Then, it reached a maximum value (211.2) at 1.0 wt% addition. Above 1.0 wt% addition, the initial permeability decreased again with a further increase in the nano-glass content. The quality factor and saturation magnetization of 0.5 wt% nano-glass added NiZnCu ferrites sintered at 880 °C was about 143 and 386 emu/cc, respectively. It was shown that the Bi - Zn - Al - B - Si - O nano-glass systems were useful as a sintering aid in the fabrication of MLCIs.
Type of Medium:
Online Resource
ISSN:
0217-9849
,
1793-6640
DOI:
10.1142/S0217984909021752
Language:
English
Publisher:
World Scientific Pub Co Pte Ltd
Publication Date:
2009