International Journal of Modern Physics B, World Scientific Pub Co Pte Ltd, Vol. 20, No. 25n27 ( 2006-10-30), p. 4040-4045
Abstract:
In the present works, the change of a rolling texture by La or Mm (Misch metal) addition in high Mg content ( 〉 5wt%) Al - Mg alloy was investigated. By Mm addition, B (Brass) orientation {011} 〈112〉 was typically developed with Mg contents and it was accelerated by La , Mm additions. TC (twin copper) orientation {255} 〈511〉 and G (Goss) orientation {110} 〈001〉 orientations closely related mechanical twinning were decreased in intensity and development of coarsen share bend was suppressed by Mm addition in Al -10wt% Mg alloy. And it caused improvement of formability by Mm addition in high Mg content Al - Mg alloy.