Abstract
A so called all-carbon based graphene field effect transistor (GFET) in which the electrodes are composed of graphite-like nano-sheets instead of metals in the traditional devices is fabricated by one-step e-beam direct writing (EBDW). It is also found that the graphite-like nano-sheets in electrodes are perpendicular to the channel graphene, which is confirmed by the transmission electron microscopy (HRTEM). The one-step fabrication of the carbonaceous electrodes is more convenient and lower-cost comparing to the preparation of traditional metal electrodes and can be applied to many other nano-electronic devices.
Similar content being viewed by others
Introduction
Graphene, a two-dimensional carbon material, has attracted wide attentions from both condensed-matter physicists and chip-makers for almost a decade1,2,3,4,5. Graphene field effect transistors (GFETs) have developed rapidly since it is considered as an option for post-silicon electronics6. In traditional GEFT devices, metal/graphene contacts for source and drain electrodes are inevitable, however, such metal/graphene contacts could seriously hinder the performances of graphene transistors, especially the high-speed traveling of the carriers7,8,9,10,11. The band-structure of graphene would be significantly altered by chemisorption on Co, Ni and Pd. In addition, the Fermi energy in graphene can be moved away from the conical points even by weak adsorption of Al, Cu, Ag, Au and Pt, which results in the doping of graphene with either electrons or holes12. The high-resolution angle-resolved photoemission studies show that substantial band gap opens in proportion to the doping effect at Ag and Cu/graphene contacts13. Especially, the modification of metal on the electronic structure of graphene not only occurs in the area underneath the metal electrodes but also affects the adjacent graphene regions hundreds nanometers away from the electrodes14,15. Besides the electronic structure, the electrical transport in graphene would also be impacted by the metal/graphene contacts. The electron-hole asymmetry and sublinear conductance as a function of carrier density mainly originate from the pinning of the charge density below the metal especially in short channel devices16,17. Therefore, a proper material for electrodes is very important for the realistic application of high-performance graphene-based devices. Carbonaceous electrode is a potential proposal for high-performance graphene-based electronics. Several groups have already made efforts towards the all-carbon electronics. Yang et al.18 reported a fabrication of all-graphene devices via layer-by-layer thinning of graphene by hydrogen-plasma etching. Wang et al.19 created all-carbon electrodes by ink jet printing with solution-processable graphene oxide sheets.
In this study, an all-carbon based GFET in which the electrodes are composed of graphite nano-sheets instead of metals has been fabricated by one-step e-beam direct writing (EBDW) on poly(methyl methacrylate) (PMMA) which is the most widely used polymeric electron resist due to its high resolution, stability and compatibility with other processing steps20,21. Although PMMA is well known as a positive e-beam resist, it can be transformed to a high-resolution (sub-10-nm) negative resist if the e-beam irradiation is high enough (overexposure)22,23,24,25,26,27,28. It is found that the negative PMMA can be graphitized by post-annealing treatment. Structural analysis including Raman scattering and high-resolution transmission electron microscopy (HRTEM) reveal that these graphitized and conductive electrodes are composed by graphite-like nano-sheets perpendicular to the channel graphene. The electrical measurements unambiguously demonstrated that the performances of such all-carbon based GFET are comparable to those of the devices with the metallic electrodes. The negative PMMA with good electrical conductivity and high-resolution is promising for the fabrication of nano-electronic devices and provides the possibility to fabricate all carbon-based GFET devices.
Results and Discussion
The technological process of the carbonaceous electrodes is illustrated in Fig. 1(a) and the details are described in the Methods. The resistivity of the carbonaceous electrode is measured to be about 4.8 × 10−3 Ω · cm [Supporting Information], which is much smaller than that of a heavily doped silicon (~10−2 Ω · cm29) and actually comparable to the in-plane resistivity for graphite(2.5–5.0 × 10−4 Ω · cm30). Therefore, such film could be good enough to act as electrodes in electronic devices.
The chemical components and structure of the annealed negative PMMA film were studied to understand the conductive mechanism. To avoid the influence of the substrate, a cross bar of the negative PMMA film was prepared on a silicon substrate, as shown in Fig. 1(b). The energy dispersive spectrometer (EDS) spectra were taken at the center of the cross bar (I) (marked by rectangles in Fig. 1(c)) and the substrate Comparing the EDS spectrum of the negative PMMA with that of the substrate, it is obvious that the negative PMMA is a carbonaceous material indeed and the oxygen atoms are almost negligible. The disappearance of oxygen atoms is caused by the volatile groups such CO2, H2 and CH3O via e-beam and annealing induced decomposition of the PMMA21,28. Figure 1(d) shows the comparison of the Raman spectrum between the bulk graphite and the negative PMMA in the Fig. 1(b). There are two obvious peaks at about 1350 and 1580 cm−1, which correspond to the D and G peaks of graphite, respectively. The G peak signifies the mono- or poly-crystalline graphite and the D peak reflects the defects and disordering of the graphite31,32,33,34,35. Although the broad 2D peak around 2700 cm−1 at the spectrum of the negative PMMA is not clear as that in the spectrum for the bulk graphite, the presence of such 2D peak corresponds to the other nano-graphites35,36,37. Therefore, the Raman measurements indicate that the prepared negative PMMA is indeedly well graphitized.
To study the detailed structure, a high-resolution transmission electron microscopy (HRTEM) was employed to analyze the negative PMMA. The sample for the HRTEM was directly prepared on a Cu grid via the same processes and conditions in the Fig. 1(a). Figure 2(a) gives a high-resolution transmission electron microscopy (HRTEM) image for the negative PMMA prepared via the same processes and conditions. The crystallization of the negative PMMA film is firstly confirmed by the selected area electron diffraction (SAED) pattern, as shown in the Fig. 2(b). From the SAED pattern, several couples of symmetrical primary diffractive spots (as marked by the circle and square boxes) and lots of random high-order diffractive spots can be seen, which indicates that the fragment is really polycrystalline. The HRETM image demonstrates that the negative PMMA consists of some crystallized nano-fragments with different crystal orientations. In addition, the embedded nano-crystals are a kind of layered structure with the spacing of ~0.34 nm, as shown by the partial zoom-in picture (Fig. 2(c)), which matches well with the layered structure of graphite30. Combination of HRTEM and Raman measurements strongly indicate that the crystallized nano-fragments in the negative PMMA are graphite nano-sheets. It is the formation of nano-fragmental and the random arrangements of the graphite sheets that cause the intense D peak and the wide 2D peak in the Raman spectrum of the negative PMMA.
The graphitization of the negative PMMA may originate from two concurrent processes: the lost of oxygen and hydrogen atoms (i.e. the deoxygenation and dehydrogenation) and the self-assembling of carbon-carbon (C-C) covalent bonds. Hydrocarbon gas can be decomposed into amorphous carbon by losing oxygen and hydrogen atoms under high-intensity electron irradiation in electron-beam-induced deposition (EBID) process38,39. Since PMMA is a kind of polymer, the macromolecular chains in PMMA would be broken into small molecular chains under electron irradiation. As long as the irradiation dose is large enough (i.e. overexposure of positive PMMA), most of the oxygen and hydrogen atoms in the film could be lost in the form of gases and only carbon atoms are left. With the dose increasing, more and more C-C bonds are cross-linked with the assistance of the so called “knock-on” effect40,41 of the high-energy e-beam irradiation, which results in the graphitization of the amorphous carbons. The higher e-beam energy, the easier it is to remove oxygen and hydrogen atoms from PMMA and induce cross-link C-C bonds in the residue. The energy of the e-beam used in our experiments is 10 keV and not high enough to directly graphitize the PMMA film well. This is the reason why the negative PMMA is almost insulated before the high-temperature annealing. The high-temperature annealing can further carbonize and graphitize the negative PMMA. Duan et al.40,42 have reported that the PMMA nano-fibers could be directly turned into graphene nano-ribbons by high-energy (200 keV) electron irradiation without high-temperature annealing, which indicates that the annealing is not necessary in preparing the conductive wires (i.e. electrodes) from PMMA if the e-beam energy is high enough.
An interesting and important phenomenon revealed by the HRTEM images is that the graphitic nano-sheets in the annealed PMMA film are “standing” rather than “lying” on the substrate. Since the HRTEM gives a top-down view of the sample, the presence of the layer-by-layer structures with the spacing of about 0.33 nm in the HRTEM images taken at different areas of the cross bar on the Cu grid indicates that the graphite sheets in the negative PMMA are perpendicular to the substrate, which is consistence with the report by Duan et al.35. The e-beam is perpendicular to the substrate in the EBL and the large e-beam energy is benefit to form the C-C bonds. Therefore, the graphitic sheets tend to align parallel to the direction of the incident e-beam. However, the energy distribution perpendicular to the e-beam is uniform which results in that the sheets extend randomly along the parallel directions of the substrate.
It is convinced that the electrode/graphene contact could be fabricated as the vertical contact between graphite sheet and graphene if the negative PMMA was used as the electrodes in GFET. Based on the analysis above, the microstructure of the all-carbon based GFET can be sketched diagrammatically, as shown in Fig. 2(d). It is reasonable to deduce that the π electrons (i.e. the delocalized electrons) in graphene could be transported easily into the graphite sheets if their π states overlap together. Just like the formation of the C-C bonds in the negative PMMA, the C-C bonds can also be formed among the carbons in the graphene and the negative PMMA by the e-beam irradiation and high-temperature annealing. In this case, the graphene in channel and the graphite-sheet in electrode are bonded together, which makes them form a whole sheet and makes their π states overlap together. Therefore, the vertical contact between the graphene in the channel and the graphite in the electrodes suppliers a quite worth strategy to reduce the impacts of electrode/graphene contacts in GFET.
Figure 3(a) shows the fabrication process for an all-carbon based GFET with the channel length from 1 to 10 μm. Before the PMMA film for fabricating the electrodes was spin-coated on the substrate, the chemical vapor deposition (CVD) grown graphene43 was transferred onto a heavily doping silicon substrate with 300 nm thickness SiO2 and etched to a ribbon with the width of 3 μm using O2 plasma with the assistant of EBL. The conductive silicon substrate is used as a back-gate of the GFET. From the scanning electron microscope (SEM) image of the Fig. 3(a), it is clear that the electrodes are well defined and the graphene ribbon is well preserved after the high-temperature annealing.
To characterize the graphene in the channel after annealing at the temperature of 800 °C, the Raman spectra of the graphene in the channel before and after the annealing were measured, as shown in Fig. 3(b). It is found that the D peak standing for the defects of the graphene does not enhance obviously, which indicates that the graphene was not damaged in the annealing process. However, the ratio of the 2D to G peaks decreased a little, which may be induced from the tighter adhesion between the substrate and graphene after the high-temperature annealing44,45. To avoid the damages to the graphene during the annealing process, the slow rising and falling rates of the temperature are necessary to weaken the impact due to the different thermal expansivities of the substrate and graphene.
Any adjacent pair of electrodes in the Fig. 3(a) could be source and drain electrodes, respectively. As shown in Fig. 3(c), the current-voltage (I–V) curves of the GFET with the different channel lengths are standard straight lines, indicating that the electrode/graphene contacts are good and without obvious barriers. The back-gated transfer characteristic curve in Fig. 3(d) also represents that the graphene transistor based on the negative PMMA electrodes is as good as that based on metal electrodes on the field-effect property. In the Fig. 3(d), the blue circles represent the measured datum of the GFET with length of 9 μm and the red solid line represents the fitting by the equation (1) in the Ref [29]. The measurement of the electrical transport properties were performed in the vacuum of ~10−4 Pa by a Keithley 4200 analyzer at room temperature and the carrier mobility of ~3700 cm2/V/s of this GFET was obtained from the fitting of the transfer characteristic curve. The Dirac point (the minimum of the transfer characteristic curve) was at about −2 V, indicating that the device was slightly n-type doped. In our previous work43, even the best GFET with the Cr/Au electrodes is heavily p-type doped with the Dirac point of about +39 V and its mobility is much smaller than that of this all-carbon based GFET. Moreover, the distinct electron-hole asymmetry (i.e. the asymmetry of the transfer characteristic curve on both sides of the Dirac point) was observed in our previous GFET with the mobility of ~2440 cm2/V/s to the electrons and ~1750 cm2/V/s to the holes, which is however not so obvious in the all-carbon based GFET as shown in the Fig. 3(d). Therefore, the negative PMMA film composed by the graphite nano-sheets is totally qualified to be the electrode material in GFET.
In summary, we have fabricated a kind of all-carbon based GFET with the carbonaceous electrodes and the channel graphene. The fabrication method of the all-carbon based GFET is simple, convenient and accurate because the electrodes are directly written out by e-beam on a PMMA film. In spite of the simpler and lower cost of the fabrication, the performance of the all-carbon based GFET is totally comparable to the metal contacted GFET from the I–V and field-effect characteristics. It is found that the carbonaceous electrodes are composed by graphite nano-sheets perpendicular to the graphene in the channel. Such vertical contacts between the graphite and graphene supplies a potential choice for the electrode/graphene contact in high-performance GFET.
Methods
Carbonaceous electrode preparation
First, a PMMA (MicroChem Corp., 950 K, 2 wt% in chlorobenzene) film was spin-coated on a SiO2/Si substrate followed by 180 °C baking on a hot-plate for 1 minute. Second, the PMMA film was irradiated by a focused e-beam (FEB) in an EBL system (FEI 600i) to define the patterns for electrodes. During the irradiation process, the accelerating voltage and the current of the FEB were 10 kV and 1.4 nA, respectively. In order to transform the PMMA film to a negative resist, the irraidaiton dose should be exceeded 50 times more than the normal dose for a positive PMMA20. Third, the irradiated film was cleaned by acetone to dissolve the unirradiated parts of the film so that the patterned negative parts of the PMMA film were left. Final, the patterned sample was annealed at 800 °C for 2 h with the protection of Ar (90% Ar + 10% H2 for actual) to improve the conductivity of the negative PMMA parts.
Additional Information
How to cite this article: Chen, W. et al. All-carbon based graphene field effect transistor with graphitic electrodes fabricated by e-beam direct writing on PMMA. Sci. Rep. 5, 12198; doi: 10.1038/srep12198 (2015).
References
Novoselov, K. S. et al. Electric Field Effect in Atomically Thin Carbon Films. Science 306, 666–669 (2004).
Geim, A. K. Graphene: Status and Prospects. Science 324, 1530–1534 (2009).
Withers, F., Bointon, T. H., Craciun, M. F. & Russo, S. All-Graphene Photodetectors. ACS Nano 7, 5052–5057 (2013).
Mueller, T., Xia, F. & Avouris, P. Graphene photodetectors for high-speed optical communications. Nat. Photonics 4, 297–301 (2010).
Lin, Y.-M. et al. Wafer-Scale Graphene Integrated Circuit. Science 332, 1294–1297 (2011).
Schwierz, F. Graphene Transistors. Nat. Nanotechnology 5, 487–496 (2010).
Lee, J., Novoselov, K. S. & Shin, H. S. Interaction between Metal and Graphene: Dependence on the Layer Number of Graphene. ACS Nano 5, 608–612 (2011).
Chen, W. et al. Current self-amplification effect of graphene-based transistor in high-field transport. Carbon 77, 1090–1094 (2014).
Liang, G., Neophytou, N., Lundstrom, M. S. & Nikonov, D. E. Contact Effects in Graphene Nanoribbon Transistors. Nano. Lett. 8, 1819–1824 (2008).
Leong, W. S., Gong, H. & Thong, J. T. L. Low-Contact-Resistance Graphene Devices with Nickel-Etched-Graphene Contacts. ACS Nano 8, 994–1001 (2014).
Chen, W. et al. Current induced doping in graphene-based transistor with asymmetrical contact barriers. Appl. Phys. Lett. 104, 083115 (2014).
Giovannetti, G. et al. Doping Graphene with Metal Contacts. Phys. Rev. Lett. 101, 026803 (2008).
Varykhalov, A., Scholz, M., Kim, T. K. & Rader, O. et al. Effect of noble-metal contacts on doping and band gap of graphene. Phys. Rev. B 82, 121101(R) (2010)
Mueller, T., Xia, F., Freitag, M., Tsang, J. & Avouris, P. Role of contacts in graphene transistors: A scanning photocurrent study. Phys. Rev. B 79, 245430 (2009).
Lee, E. J. H., Balasubramanian, K., Weitz, R. T., Burghard, M. & Kern, K. Contact and edge effects in graphene Devices. Nat. Nanotechnology 1–5 (2008).
Nouchi, R. & Tanigaki, K. Charge-density depinning at metal contacts of graphene field-effect transistors. Appl. Phys. Lett. 96, 253503 (2010).
Huard, B., Stander, N., Sulpizio, J. & Goldhaber-Gordon, D. Evidence of the role of contacts on the observed electron-hole asymmetry in graphene. Phys. Rev. B 78, 121402(R) (2008).
Yang, R. et al. Fabrication of high-quality all-graphene devices with low contact resistances. Nano Research 7, 1449–1456 (2014).
Wang, S. et al. High mobility, printable and solution-processed graphene electronics. Nano Lett. 10, 92–98 (2009).
Broers, A. N., Harper, J. M. E. & Molzen, W. W. 250Å linewidths with PMMA electron resist. Appl. Phys. Lett. 33, 392–394 (1978).
Duan, H., Zhao, J., Zhang, Y., Xie, E. & Han, L. Preparing patterned carbonaceous nanostructures directly by overexposure of PMMA using electron-beam lithography. Nanotechnology 20, 135306 (2009).
Zailer, I., Frost, J., Chabasseur-Molyneux, V., Ford, C. & Pepper, M. Crosslinked PMMA as a high-resolution negative resist for electron beam lithography and applications for physics of low-dimensional structures. Semicond. Sci. Technol. 11, 1235–1238 (1996).
Liu, Y., Xu, X., Xing, B., Yu, Y. & Yu J. Fabrication of a Low-Loss SSC Using High-Dose Electron Beam Lithography Exposure With Negative PMMA Resist. IEEE Photonics Technology Letters 22, 501–503 (2010).
Ressier, L. et al. Fabrication of planar cobalt electrodes separated by a sub-10 nm gap using high resolution electron beam lithography with negative PMMA. Ultramicroscopy 107, 985–988 (2007).
Hoole, A., Welland, M. & Broers, A. Negative PMMA as a high-resolution resist—the limits and possibilities. Semicond. Sci. Technol. 12, 1168–1170 (1997).
Duan, H. G. Sub-10-nm half-pitch electron-beam lithography by using pol(methyl methacrylate) as a negative resist. J. Vac. Sci. Technol. B 28, C6C58 (2010).
Koval, Y. Mechanism of etching and surface relief development of PMMA under low-energy ion Bombardment. J. Vac. Sci. Technol. B 22, 843–851 (2004).
Lee, E. H., Rao, G. R. & Mansur, L. K. LET effect on cross-linking and scission mechanisms of PMMA during irradiation. Radiat. Phys. Chem. 55, 293–305 (1999).
Fripp, A. L. & Slack, L. H. Resistivity of Doped Polycrystalline Silicon Films. J. Electrochem. Soc: Solid-State Science and Technology 145–146 (1973).
Pierson, H. O. Handbook of carbon, graphite, diamond and fullerenes: properties, processing and applications . Ch. 5, p61 (William Andrew, Noyes, 1993).
Tuinstra, F. & Koenig, J. L. Raman Spectrum of Graphite. J. Chem. Phys. 53, 1126–1130 (1970).
Ferrari, A. C. & Robertson, J. Interpretation of Raman spectra of disordered and amorphous carbon. Phys. Rev. B 61, 14095 (2000).
Ferrari, A. C. et al. Raman Spectrum of Graphene and Graphene Layers. Phys. Rev. Lett. 97, 187401 (2006).
Calizo, I., Balandin, A. A., Bao, W., Miao, F. & Lau, C. N. Temperature Dependence of the Raman Spectra of Graphene and Graphene Multilayers. Nano. Lett. 7, 2645–2649 (2007).
Ferrari, A. C. Raman spectroscopy of graphene and graphite: Disorder, electron–phonon coupling, doping and nonadiabatic effects. Solid State Communication 143, 47–57 (2007).
Cancado, L. G. et al. Anisotropy of the Raman spectra of nanographite ribbons. Phys. Rev. Lett. 93, 047403 (2004).
Cancado, L. G. et al. Stokes and anti-Stokes double resonance Raman scattering in two-dimensional graphite. Phys. Rev. B 66, 035415 (2002).
Randolph, S. J., Fowlkes, J. D. & Rack, P. D. Focused, Nanoscale Electron-Beam-Induced Deposition and Etching. Crit. Rev. Solid StateMater. Sci. 31, 55–89 (2006).
van Dorp, W. F., van Someren, B., Hagen, C. W., Kruit, P. & Crozier, P. A. Approaching the Resolution Limit of Nanometer-Scale Electron Beam-Induced Deposition. Nano Lett. 5, 1303–1307 (2005).
Duan H. G., Xie, E., Han, L. & Xu, Z. Turning PMMA Nanofibers into Graphene Nanoribbons by In Situ Electron Beam Irradiation. Adv. Mater. 20, 3284–3288 (2008).
Yuzvinsky, T. D. et al. Shrinking a Carbon Nanotube. Nano Lett. 12, 2718–2722 (2006).
Duan, H. G., Xie, E. & Han, L. Turning electrospun poly(methyl methacrylate) nanofibers into graphitic nanostructures by in situ electron beam irradiation. J. Appl. Phys. 103, 046105 (2008).
Wang, C. C. et al. Growth of Millimeter-Size Single Crystal Graphene on Cu Foils by Circumfluence Chemical Vapor Deposition. Sci. Rep. 4, 4537 (2014).
Ni, Z. H. et al. Tunable Stress and Controlled Thickness Modification in Graphene by Annealing. ACS Nano. 2, 1033–1039 (2008).
Berciaud, S., Ryu, S. Brus, L. E. & Heinz, T. F. Probing the Intrinsic Properties of Exfoliated Graphene: Raman Spectroscopy of Free-Standing Monolayers. Nano. Lett. 9, 346–352 (2009).
Acknowledgements
This work was supported by the National Natural Science Foundation of China (Nos. 11104347, 11104348 and 11104349), the open foundation based on the innovation platform of Hunan key laboratories (No. 13K022) and the open foundation of State Key Laboratory of high Performance Computing (No. 201301–02).
Author information
Authors and Affiliations
Contributions
L.W. and X.Z. conceived and designed the experiments. W.C. performed the experiments. Y.Y., X.Z. and C.W. prepared the graphene samples. F.W., G.W. and F.Y. contributed analysis tools and assisted the experiments. L.W., G.P. and S.Q. supervised the project. W.C., L.W. and X.Z. co-wrote the paper. All authors discussed the results and analyzed the data and commented on the manuscript.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Electronic supplementary material
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Chen, W., Yu, Y., Zheng, X. et al. All-carbon based graphene field effect transistor with graphitic electrodes fabricated by e-beam direct writing on PMMA. Sci Rep 5, 12198 (2015). https://doi.org/10.1038/srep12198
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep12198
This article is cited by
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.