Abstract
The mechanism of continuous dissolution was studied using transmission electron microscopy, X-ray diffraction and hardness measurements. The metastable α′ phase was identified in the first stage of dissolution nucleating at the α-η boundaries. Interface dislocations at the α-α′ boundaries forming a perpendicular net in the 〈110〉 directions were identified as of screw character and of Burgers vector b=1/2a 〈110〉. During dissolution a change of shape of α′ precipitates occurs leading to their fragmentation and to a change of the direction of boundaries into 〈110〉 directions.
Similar content being viewed by others
References
K. Russew and W. Gust, Z. Metallkde 70 (1979) 522.
A. Pawłowski and W. Truszkowski, Acta Metall 30 (1982) 37.
T. H. Chuang, Doktorarbeit, Max-Planck-Institut für Metallforschung, Stuttgart, (1983).
I. G. Solorzano, G. R. Purdy and G. C. Weatherly, Acta Metall. 32 (1984) 1709.
P. Zięba and A. Pawłowski, Archiwum Hutnictwa 31 (1986) 597.
S. A. Hackney and F. S. Biancaniello, Scripta Metall. 20 (1986) 1417.
M. Bourchard, R. J. Livak and G. Thomas, Surface Sci. 31 (1975).
È. P. Butler, Proceedings of the International Conference on Solid → Solid Phase Transformation, edited by H. I. Aaronson, D. E. Laughlin, R. F. Sekerka, and C. M. Wayman (The Metal Society, AIME, New York, 1982) p. 673.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Dutkiewicz, J., Pawłowski, A. & Zięba, P. The mechanism of continuous dissolution of the lamellar structure in aged Al 22 at% Zn alloy. J Mater Sci 23, 2768–2771 (1988). https://doi.org/10.1007/BF00547449
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00547449