Keywords:
aromatic polyamides
;
silica
;
sol-gel process
;
organic-inorganic hybrid materials
;
gelation
;
thermogravimetric analysis
Source:
Springer Online Journal Archives 1860-2000
Topics:
Chemistry and Pharmacology
,
Mechanical Engineering, Materials Science, Production Engineering, Mining and Metallurgy, Traffic Engineering, Precision Mechanics
,
Physics
Notes:
Summary A new kind of organic-inorganic hybrid composite was prepared by means of the sol-gel process. The polymer employed was a mixed-isomer aromatic polyamide having good solubility and thermal stability. The silica constituting the inorganic phase was produced by the hydrolysis and condensation of tetramethoxysilane. The bonding between the phases involved aminophenyl-trimethoxysilane, in which the amino group can react with the phthaloyl chloride end-capped polymer, and the methoxysilane groups undergo hydrolysis. The composition of these composites was varied by changing the linear polymer chain length and relative amount of tetramethoxysilane. The gelation time was found to range from a few minutes to several days. Thermogravimetric analyses showed that decomposition starts at approximately 450 °C. Thin films cast from materials having a relatively high silica content were opaque and rigid, but those with low silica content were flexible and transparent.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1007/BF00692959
Permalink