In:
Key Engineering Materials, Trans Tech Publications, Ltd., Vol. 627 ( 2014-9), p. 169-172
Kurzfassung:
To solve the problem of large environmental burden caused by disposal of FRP (Fiber Reinforced Plastics), Poly Lactic Acid (PLA), which is plant-derived and biodegradable, has received a lot of attention as an environmentally friendly material for the matrix of FRP. However, since the decomposition rate is very slow as compared with other biodegradable resins, it is difficult to make a processing of a large amount of PLA in the natural environment. Therefore, a method to accelerate decomposition rate of PLA by blending hydrolysis accelerator to PLA has been developed. In this study, composite material, in which PLA is blended with hydrolysis accelerator and reinforced with glass fibers, was molded using high speed compression molding process, and its tensile strength and the effect of heat treatment and tensile strength on the crystallinity was clarified. In consequence, regardless of the existence of hydrolysis accelerator, crystallinity of glass fiber reinforced PLA composites was improved by the annealing process. Tensile strength of glass fiber reinforced PLA decreased by the annealing process. For glass fiber reinforced PLA which was blended with hydrolysis accelerator, however, annealing process did not affect their tensile strength.
Materialart:
Online-Ressource
ISSN:
1662-9795
DOI:
10.4028/www.scientific.net/KEM.627
DOI:
10.4028/www.scientific.net/KEM.627.169
Sprache:
Unbekannt
Verlag:
Trans Tech Publications, Ltd.
Publikationsdatum:
2014
ZDB Id:
2073306-9
Permalink