Description / Table of Contents:
Summary Microtome cuts of partially crystalline injection mouldings (PE, PP, POM) were taken out of different cross-section layers and analysed with the polarization microscope, the DTA/DSC-analysis and by density measurements. The crystallinity and morphological structure are strongly inhomogeneous according to the different cooling and flow conditions across the cross-section. With linear polyethylene the zone of the highest crystallinity lies closely under the moulding's surface. In differential thermal analysis a typical double melting peak appears with samples of this range. In the tensile test these zones show a small elongation at fracture, whereas the marginal and core layers behave ductily.
Notes:
Zusammenfassung Es wurden Mikrotomschnitte von teilkristallinen Spritzgußteilen (PE, PP, POM) aus verschiedenen Querschnittstiefen entnommen und mit dem Polarisationsmikroskop, der DTA/DSC-Analyse sowie durch Dichtemessungen untersucht. Die Kristallinität und Gefügestruktur sind entsprechend den unterschiedlichen Abkühl- und Fließbedingungen über dem Querschnitt stark inhomogen. Bei linearem Polyäthylen liegt die Zone höchster Kristallinität dicht unterhalb der Formteiloberfläche. Bei der Differential-thermoanalyse tritt bei Proben aus diesem Bereich ein typischer Doppelschmelzpeak auf. Im Zugversuch weisen diese Zonen eine geringe Bruchdehnung auf, während sich die Rand- und Kernschichten duktil verhalten.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1007/BF01384025
Permalink