Materials Science Forum, Trans Tech Publications, Ltd., Vol. 944 ( 2019-1), p. 351-356
Abstract:
The microstructure and mechanics of 15CrNiMo steel with different quenching temperatures (800°C, 825°C, 850°C, 875°C, 900°C) and different quenching holding time (15min, 25min, 35min) were studied for steel 15CrNiMo for roller bit. The relationship between the properties of different quenching parameters and the mechanical properties such as microstructure, impact toughness and hardness was analyzed. The results show that the microstructure of the annealed precursor is mainly ferrite and pearlite. With the increase of quenching temperature, the ferrite is gradually reduced, the lath martensite is gradually increased, and the martensite grains tend to grow. The strength increases first and then decreases, and the plasticity increases slightly. The quenching and holding time has no obvious effect on the test steel, and the austenitization of the core is the best time. The best quenching temperature is 850°C, the best holding time is 25 min, (tempering temperature is 220°C, tempering holding time is 50 min) and the mechanical properties are optimal.
Type of Medium:
Online Resource
ISSN:
1662-9752
DOI:
10.4028/www.scientific.net/MSF.944
DOI:
10.4028/www.scientific.net/MSF.944.351
Language:
Unknown
Publisher:
Trans Tech Publications, Ltd.
Publication Date:
2019
detail.hit.zdb_id:
2047372-2
Permalink