Japanese Journal of Applied Physics, IOP Publishing, Vol. 49, No. 12R ( 2010-12-01), p. 121103-
Abstract:
NiO films were grown on a Pt substrate by radio frequency (RF) magnetron sputtering using a NiO ceramic target. A crystalline NiO phase with the [111] preferred orientation was formed for the films grown above 100 °C. Resistance switching behavior was not observed in the NiO films annealed in the air or in ambient O 2 after film deposition. However, the NiO films annealed in ambient N 2 exhibited resistance switching properties. The stability of the switching voltage was considerably influenced by the oxygen to argon ratio during film growth. In particular, the NiO film grown under an 8.0 mTorr oxygen partial pressure exhibited stabilized switching voltages ( V set ∼1.45±0.20 V and V reset ∼0.62±0.09 V). Therefore, the control of the ambient gas pressure during the growth and annealing of the NiO films was important for obtaining good resistance switching properties.
Type of Medium:
Online Resource
ISSN:
0021-4922
,
1347-4065
DOI:
10.1143/JJAP.49.121103
Language:
Unknown
Publisher:
IOP Publishing
Publication Date:
2010
detail.hit.zdb_id:
218223-3
detail.hit.zdb_id:
797294-5
detail.hit.zdb_id:
2006801-3
detail.hit.zdb_id:
797295-7
Permalink