Applied Mechanics and Materials, Trans Tech Publications, Ltd., Vol. 860 ( 2016-12), p. 87-92
Abstract:
This paper reports on fabricated hard magnetic cobalt nickel phosphorous (CoNiP) films with electro-chemically deposition technique on copper substrate in the presence of different urea (0 to 10 g/L) and NaH 2 PO 2 (16 to 21 g/L) concentrations. Thin films were obtained at current density ranges from 5 to 20 mA/cm 2 and temperature varies from ambient temperature to 60°C. Magnetic properties namely coercivity, remanent magnetization, saturation magnetization and squareness of the films were studied using Vibrating Sample Magnetometer (VSM). The result showed that for bath containing higher concentration of urea (10 g/L), bright films with higher coercivity were obtained at moderate current density (15 mA/cm 2 ) and at higher temperatures (40-60°C). In contrary, uniform and bright films were produced at ambient temperature in bath containing no urea or lower concentration of urea. Scanning Electron Microscopy (SEM) revealed that porosity and cracking tendency are increased with increasing temperature. CoNiP thin films with improved magnetic properties are thus obtained for plausible applications in high density recording media and MEMS.
Type of Medium:
Online Resource
ISSN:
1662-7482
DOI:
10.4028/www.scientific.net/AMM.860
DOI:
10.4028/www.scientific.net/AMM.860.87
Language:
Unknown
Publisher:
Trans Tech Publications, Ltd.
Publication Date:
2016
detail.hit.zdb_id:
2251882-4
Permalink