This letter reports on the effect of the energy Ebi, delivered to the sputtered Ti(Al,V)N film by bombarding ions, on its microstructure, macrostress σ, mechanical properties, and resistance to cracking. The films were deposited by reactive magnetron sputtering. Interrelationships between these parameters were investigated in detail. It was shown that (1) the increase of the energy Ebi makes it possible to convert (1) the film microstructure from columnar to dense, noncolumnar, (2) the macrostress σ from tensile (σ & gt; 0) to compressive (σ & lt; 0), (3) the brittle hard film with low ratio H/E* & lt; 0.1 and low elastic recovery We & lt; 60% to the flexible hard film with high ratio H/E* ≥ 0.1 and high elastic recovery We ≥ 60%, (2) the flexible hard Ti(Al,V)N films with high ratio H/E* ≥ 0.1, high elastic recovery We ≥ 60%, and compressive macrostress can be formed not only in the transition zone (zone T in which the films exhibit a dense, voids-free microstructure) of the Thornton's structural zone model (SZM) but also in zone 1 in which the films exhibit a columnar microstructure and (3) the line corresponding to the films with zero macrostress (σ = 0) in the SZM lies in zone 1 corresponding to the columnar microstructure; here, H is the film hardness and E* = E(1 − ν2) is the effective Young's modulus, E is the Young's modulus, and ν is the Poisson's ratio.
Type of Medium:
Online Resource
ISSN:
0734-2101
,
1520-8559
Language:
English
Publisher:
American Vacuum Society
Publication Date:
2017
detail.hit.zdb_id:
1475424-1
detail.hit.zdb_id:
797704-9
Permalink