High Temperature Materials and Processes, Walter de Gruyter GmbH, Vol. 35, No. 4 ( 2016-04-1), p. 417-423
Abstract:
Zn 0.5 Ni 0.5- x Co x Fe 2- y La y O 4 ferrites (with x =0, 0.02 and y =0, 0.02) were prepared by an industrial method using the standard ceramic technique and sintered at 1,250°C in air. X-ray diffraction (XRD) was used to obtain the phase formation of the NiZn ferrites. The microstructure of ferrites was investigated by scanning electron microscopy (SEM). The XRD reveals that lattice parameter ( a ) is decreased and a secondary phase (LaFeO 3 ) is formed in the La–Co co-substituted NiZn ferrite sample, meanwhile, the grain size ( D ) of this sample decreased obviously by observing SEM photographs. Vibrating sample magnetometry (VSM), B-H analyzer, impedance analyzer and electrometer were carried out in order to characterize some properties of the ferrites. This investigation indicates that, La–Co co-substituted NiZn ferrite sample has higher power loss ( P cv ) than other samples at low frequency with an increase in coercive field ( H c ) and magnetocrystalline anisotropy ( K 1 ), a decrease in initial permeability ( μ i ) and saturation magnetization ( M s ). However, at high frequency, the power loss of La–Co co-substituted sample is low, which is attributed to high resistivity ( ρ ), small grain size ( D ), less number of Fe 2+ ions and low porosity ( P ).
Type of Medium:
Online Resource
ISSN:
0334-6455
,
2191-0324
DOI:
10.1515/htmp-2014-0221
Language:
Unknown
Publisher:
Walter de Gruyter GmbH
Publication Date:
2016
detail.hit.zdb_id:
2602423-8
Permalink