Applied Physics Letters, AIP Publishing, Vol. 81, No. 24 ( 2002-12-09), p. 4532-4534
Abstract:
Filling-factor tunable titanium dioxide replicas of colloidal crystals were fabricated by using a liquid phase deposition (LPD) technique. Ammonium hexafluorotitanate [(NH4)2TiF6] was used as a precursor, which was converted slowly to titanium dioxide by hydrolysis with boric acid. After the oxide was formed in voids of latex colloidal crystals, the latex was removed by calcination. By applying the LPD process to the replica again, the filling factor of the replica could be increased in a controllable fashion. With 203 nm template spheres, the peak shift in the ∼490 nm stop band depended linearly on the deposition time for the first 20 min, at a rate of 4.4 nm/min. Thus the position of the Bragg reflection peak could be adjusted precisely by controlling the filling factor of the replica structure.
Type of Medium:
Online Resource
ISSN:
0003-6951
,
1077-3118
Language:
English
Publisher:
AIP Publishing
Publication Date:
2002
detail.hit.zdb_id:
211245-0
detail.hit.zdb_id:
1469436-0
Permalink