In:
Advanced Materials, Wiley, Vol. 33, No. 48 ( 2021-12)
Abstract:
Due to their exceptional catalytic properties for the oxygen reduction reaction (ORR) and other crucial electrochemical reactions, PtCo intermetallic nanoparticle (NP) and single atomic (SA) Pt metal site catalysts have received considerable attention. However, their formation mechanisms at the atomic level during high‐temperature annealing processes remain elusive. Here, the thermally driven structure evolution of Pt–Co binary catalyst systems is investigated using advanced in situ electron microscopy, including PtCo intermetallic alloys and single Pt/Co metal sites. The pre‐doping of CoN 4 sites in carbon supports and the initial Pt NP sizes play essential roles in forming either Pt 3 Co intermetallics or single Pt/Co metal sites. Importantly, the initial Pt NP loadings against the carbon support are critical to whether alloying to L1 2 ‐ordered Pt 3 Co NPs or atomizing to SA Pt sites at high temperatures. High Pt NP loadings (e.g., 20%) tend to lead to the formation of highly ordered Pt 3 Co intermetallic NPs with excellent activity and enhanced stability toward the ORR. In contrast, at a relatively low Pt loading ( 〈 6 wt%), the formation of single Pt sites in the form of PtC 3 N is thermodynamically favorable, in which a synergy between the PtC 3 N and the CoN 4 sites could enhance the catalytic activity for the ORR, but showing insufficient stability.
Type of Medium:
Online Resource
ISSN:
0935-9648
,
1521-4095
DOI:
10.1002/adma.202106371
Language:
English
Publisher:
Wiley
Publication Date:
2021
detail.hit.zdb_id:
1012489-5
detail.hit.zdb_id:
1474949-X
Permalink