Clay Minerals, Mineralogical Society, Vol. 56, No. 1 ( 2021-03), p. 28-36
Abstract:
NaY zeolite was synthesized from kaolin/dimethyl sulfoxide (DMSO) intercalation composites using an in situ crystallization technique. The effects of the intercalation ratios and the amounts of the kaolin/DMSO intercalation composite on the synthesis of an NaY zeolite molecular sieve were studied. The samples were characterized by X-ray diffraction, Fourier-transform infrared spectroscopy, differential thermal analysis, N 2 adsorption–desorption and scanning electron microscopy. In the in situ synthesis system, when the kaolin/DMSO intercalation composite was added, pure NaY zeolite was formed. By increasing the amount of kaolin/DMSO intercalation composite added, the crystallinity of the samples increased, and after reaching the maximum amount of kaolin/DMSO intercalation composite added, the crystallinity decreased with further increases of the amount of kaolin/DMSO intercalation composite added. To higher intercalation ratio, the crystallinity can be greatly improved at the lower addition content. At an intercalation ratio of 84%, the added amount of kaolin/DMSO intercalation composite was 2.5% and the crystallinity of the NaY zeolite molecular sieve reached a maximum value of 45%. At intercalation ratios of 55% and 22%, the amount of kaolin/DMSO intercalation composite added was 15% and the crystallinities of the NaY zeolite molecular sieves were 44% and 47%, respectively. The NaY zeolite has good thermal stability and a particle diameter of ~0.5 μm. The Brunauer–Emmett–Teller (BET) specific surface area and pore volume of the sample were 519 m 2 g –1 and 0.355 cm 3 g –1 , respectively.
Type of Medium:
Online Resource
ISSN:
0009-8558
,
1471-8030
Language:
English
Publisher:
Mineralogical Society
Publication Date:
2021
detail.hit.zdb_id:
2036186-5
detail.hit.zdb_id:
961059-5
SSG:
13
Permalink