Journal of Materials Chemistry C, Royal Society of Chemistry (RSC), Vol. 11, No. 38 ( 2023), p. 13030-13038
Abstract:
Cu-based halide perovskites have attracted extensive attention in the optoelectronic field owing to their non-toxic nature and excellent stability. Nevertheless, the growth mechanism of Cu-based halide perovskite nanocrystals (NCs) remains unclear, and the size and uniformity of NCs are difficult to control, which seriously hinders the development of these materials. Herein, a facile hot-injection method was applied to control the size and uniformity of blue-emitting (450 nm) Cs 3 Cu 2 I 5 NCs. The dimensions of Cu-based perovskites were tuned from zero-dimensional NCs to one-dimensional nanorods. Additionally, the sizes of Cs 3 Cu 2 I 5 NCs could be tuned from 22.1 ± 1.5 to 8.9 ± 1.1 nm by varying the reaction temperature and the dosage of cesium oleate, which is also extended to tune the size of Cs 3 Cu 2 X 5 (X = Br and Cl) NCs. Interestingly, the photoluminescence (PL) maximum at 450 nm was almost unchanged with the size tuning, indicating that PL is from the radiation recombination of self-trap exciton emission. Moreover, the phase transition temperature of Cs 3 Cu 2 X 5 NCs was regulated by varying the size, where a small size is beneficial to the decrease of the phase transition temperature. As a demonstration, the different-sized Cs 3 Cu 2 X 5 NCs exhibited a size-dependent temperature response, and the response time became shorter as the size decreased. The temperature response of the small-sized Cs 3 Cu 2 X 5 NCs could be decreased to only 15 s, which is better than that of their counterparts reported previously. This work may deepen the understanding of the size-dependent phase transition process in Cu-based perovskite NCs.
Type of Medium:
Online Resource
ISSN:
2050-7526
,
2050-7534
Language:
English
Publisher:
Royal Society of Chemistry (RSC)
Publication Date:
2023
detail.hit.zdb_id:
2702245-6
Permalink