Corrosion, Association for Materials Protection and Performance (AMPP), Vol. 34, No. 2 ( 1978-02-01), p. 52-60
Abstract:
This investigation is concerned with the effect of chromium and molybdenum on the formation of the passive film of stainless steels, and its corrosion resistance to the chloride ion. The corrosion resistance to the chloride ion was estimated by the potential decay method and the measurement of the anodic polarization curve. The composition analysis of the passive film was performed by Auger Electron Spectroscopic Analysis. The following conclusions were obtained from the test results: (1) The passive film was more resistant in the environment containing chloride ions as the chromium content in the passive film increased, and (2) molybdenum was observed on AES analysis to have an effect on the increment of the chromium content in the passive film and to promote the passive film formation of stainless steels, probably adsorbing on the active metal surface in the form of molybdate.
Type of Medium:
Online Resource
ISSN:
1938-159X
,
0010-9312
DOI:
10.5006/0010-9312-34.2.52
Language:
English
Publisher:
Association for Materials Protection and Performance (AMPP)
Publication Date:
1978
detail.hit.zdb_id:
217266-5
detail.hit.zdb_id:
2043065-6
Permalink