Acta Physica Sinica, Acta Physica Sinica, Chinese Physical Society and Institute of Physics, Chinese Academy of Sciences, Vol. 53, No. 3 ( 2004), p. 844-
Abstract:
Electrical-resistivity measurements between 1.5 K and 300 K were performed on the Zr46.75Ti8.25Cu7.5Ni10Be27.5 bulk metallic glasses (BMGs) before and after annealing. Results of the superconducting transition temperature measurements are presented for the BMG Zr46.75Ti8.25Cu7.5Ni10Be27.5. The superconducting critical temperature Tc is 1.84K for the as-prepared metallic glassy sample and 3.76K for the annealed sample at zero magnetic fields. The as-prepared metallic glassy sample exhibits negative temperature coefficient of the resistivity in the temperature range from 5 to 300 K. The negative temperature coefficient of the resistivity of the as-prepared metallic glassy sample can be reasonably understood with the extended Faber-Ziman theory in terms of the diffraction model for metallic glasses if it is assumed that Zr, Ti, Cu, Ni and Be contribute 1.5, 1.5, 0.5, 0.5 and 2 conduction electrons, respectively. The R(T) of the BMG Zr46.75Ti8.25Cu7.5Ni10Be27.5 over the temperature range from 5 to 300 K was analyzed by fitting it to a polynomial using a least-squares procedure.
Type of Medium:
Online Resource
ISSN:
1000-3290
,
1000-3290
Language:
Unknown
Publisher:
Acta Physica Sinica, Chinese Physical Society and Institute of Physics, Chinese Academy of Sciences
Publication Date:
2004
Permalink