Materials Science Forum, Trans Tech Publications, Ltd., Vol. 449-452 ( 2004-3), p. 377-380
Abstract:
Electroplating behavior of Bi 2 Te 3 and thermoelectric properties of the electroplated Bi 2 Te 3 films were investigated for nanowire application. Composition, microstructure, and thermoelectric properties of the electroplated Bi-Te films were strongly dependent upon composition of the electroplating solutions and plating current density. While the power factor of the Bi 2 Te 3 film plated at a current density of 1×10 -4 A/cm 2 was 1.75×10 -4 W/K 2 -m, the film formed at 5×10 -4 A/cm 2 exhibited the value of 3.5×10 -4 W/K 2 -m. Substantial pore filling was achieved with electrodeposition of Bi 2 Te 3 for the alumina template with 200 nm pores.
Type of Medium:
Online Resource
ISSN:
1662-9752
DOI:
10.4028/www.scientific.net/MSF.449-452
DOI:
10.4028/www.scientific.net/MSF.449-452.377
Language:
Unknown
Publisher:
Trans Tech Publications, Ltd.
Publication Date:
2004
detail.hit.zdb_id:
2047372-2
Permalink