Journal of the American Ceramic Society, Wiley, Vol. 97, No. 9 ( 2014-09), p. 2973-2979
Abstract:
The crystallization of lead zirconate titanate ( PZT ) thin films was evaluated on two different platinum‐coated Si substrates. One substrate consisted of a Pt coating on a Ti adhesion layer, whereas the other consisted of a Pt coating on a TiO 2 adhesion layer. The Pt deposited on TiO 2 exhibited a higher degree of preferred orientation than the Pt deposited on Ti (as measured by the Full Width at Half Maximum of the 111 peak about the sample normal). PZT thin films with a nominal Zr/Ti ratio of 52/48 were deposited on the substrates using the inverted mixing order ( IMO ) route. Phase and texture evolution of the thin films were monitored during crystallization using in situ X‐ray diffraction at a synchrotron source. The intensity of the Pt 3 Pb phase indicated that deposition on a highly oriented Pt/TiO 2 substrate resulted in less diffusion of Pb into the substrate relative to films deposited on Pt/Ti. There was also no evidence of the pyrochlore phase influencing texture evolution. The results suggest that PZT nucleates directly on Pt, which explains the observation of a more highly oriented 111 texture of PZT on the Pt/TiO 2 substrate than on the Pt/Ti substrate.
Type of Medium:
Online Resource
ISSN:
0002-7820
,
1551-2916
DOI:
10.1111/jace.2014.97.issue-9
Language:
English
Publisher:
Wiley
Publication Date:
2014
detail.hit.zdb_id:
2008170-4
detail.hit.zdb_id:
219232-9
Permalink