Molecules, MDPI AG, Vol. 28, No. 4 ( 2023-02-06), p. 1554-
Abstract:
In this study, an ionogel electrolyte (PAIM-X) consisting of 1-vinyl-3-methylimidazole bis (trifluoromethyl sulfonyl) imide ([VMIM][TFSI] ), Polyacrylamide (PAAm), and MXene were prepared. The conductivity of PAIM-X and integral area of the voltammetric curve of the supercapacitor (PAIMSC) were improved by adding MXene. The addition of [VMIM][TFSI] enhanced the conductivity and applicable temperature of the ionogel electrolyte. At 90 °C, the conductivity of PAIM-4 can reach 36.4 mS/cm. In addition, spherical polyaniline with good electrochemical properties was synthesized and coated on graphite paper as an active substance. An all-solid-state supercapacitor was composed of PAIM-4, polyaniline electrode with 1.2 V potential window, pseudo-capacitors and high quality capacitors. The solvent 1-ethyl-3-methylimidazolium bis (trifluoromethyl sulfonyl imide) ([EMIM][TFSI] ) and methanesulfonic acid (MSA) were introduced into the ionogel to promote the redox reaction of polyaniline (PANI). The mass specific capacitance of PAIMSC was 204.6 F/g and its energy density could reach 40.92 Wh/kg, which shows great potential for practical application at high temperature. The device had good rate performance and cycle performance, and its capacitance retention rate was still 91.56% after 10,000 cycles. In addition, the supercapacitor can work within the temperature range of −20 °C to 90 °C. These excellent electrochemical properties indicate that PAAm/IL/Mxene-X has broad application space and prospect.
Type of Medium:
Online Resource
ISSN:
1420-3049
DOI:
10.3390/molecules28041554
Language:
English
Publisher:
MDPI AG
Publication Date:
2023
detail.hit.zdb_id:
2008644-1
Permalink