In:
Defect and Diffusion Forum, Trans Tech Publications, Ltd., Vol. 403 ( 2020-9), p. 75-89
Abstract:
The present paper explores the effects of deep cryogenic treatment (DCT) on the properties of WC-Co cemented carbides. The investigation involved four different cemented carbide (CC) grades. Two of them were coarse-grained WC with grain sizes larger than 6 μm and binder fractions of 10 and 15 wt. %. The other two were fine-grained with WC grains of 0.5-0.8 μm and the same binder fractions of 10 and 15 wt. %. Their specimens were ground and polished to prepare them for DCT. In each specimen, one half of this polished surface was used for testing the properties of the CC before cryogenic treatment. The post-DCT properties were then determined on the other half. Properties of the cemented carbides prior to and after DCT were studied using optical and scanning electron microscopy, X-ray diffraction, hardness testing according to Vickers scale followed by calculation of fracture toughness K IC and a ball-on-disk test of the wear resistance of the surface. One of the findings was that cryogenic treatment led to a decrease in residual stresses and to lower fracture toughness K IC in the CC.
Type of Medium:
Online Resource
ISSN:
1662-9507
DOI:
10.4028/www.scientific.net/DDF.403
DOI:
10.4028/www.scientific.net/DDF.403.75
Language:
Unknown
Publisher:
Trans Tech Publications, Ltd.
Publication Date:
2020
detail.hit.zdb_id:
2051135-8
Permalink