Advanced Materials Research, Trans Tech Publications, Ltd., Vol. 399-401 ( 2011-11), p. 211-215
Kurzfassung:
There are lath martensite and a little austenite in the microstructure of samples quenched. The original austenite grain sizes ranges from 7.9μm to 74.1μm, which grows up gradually with the increasing of temperature quenching. So do the martensite acicular bundle. During the process of tempering at different temperatures after quenching at 1050°C, austenite grain size becomes bigger with the temperature increasing, and martensite acicular bundle becomes thinner. The content of austenite ascends to the peak at 650°C then it decreases. The mechanical properties (σb =958.87 MPa, δ=20.44%, HRC=30.9) of the samples are the best, when quenching temperature is 1050°C and tempering temperature is 600°C.
Materialart:
Online-Ressource
ISSN:
1662-8985
DOI:
10.4028/www.scientific.net/AMR.399-401
DOI:
10.4028/www.scientific.net/AMR.399-401.211
Sprache:
Unbekannt
Verlag:
Trans Tech Publications, Ltd.
Publikationsdatum:
2011
ZDB Id:
2265002-7
Permalink