Inorganic Chemistry Frontiers, Royal Society of Chemistry (RSC), Vol. 10, No. 5 ( 2023), p. 1574-1586
Abstract:
Solid Lewis acid catalysts are commonly used in the synthesis of methyl lactate (MLA). However, water as a solvent, reactant, or by-product adsorbed on the Lewis acid sites (LAS) resulted in the deactivation of the LAS. In this study, highly dispersed In–Sn oxide on the surface of an alumina support was prepared using interconnected In 2 O 3 and SnO 2 . The highly dispersed In–Sn oxides effectively decreased the OH groups of the catalyst, leading to the decrease of the residual organics and inhibiting the deleterious effect of water on LAS. Besides, the Sn doping resulted in abundant coordinatively unsaturated sites (CUS) on the catalyst surface. The CUS were further partially hydrolyzed, forming new OH groups under the action of water during the MLA synthesis, thus leading to an increase in the LAS activity. Therefore, after the Sn doping, more LAS were detected in the presence of water, confirming that the In x Sn 10− x O y /Al 2 O 3 catalyst had more water-tolerant LAS. Under the synergy of lower hydroxyl density and more water-tolerant LAS, an MLA yield of 57.6% was achieved on the In 7 Sn 3 O y /Al 2 O 3 catalyst, which is the highest reported for the non-zeolite metal oxide catalysts up to now. This work provided a new strategy for the design of non-zeolite metal oxide catalysts with decreased OH groups, increased CUS and no LAS deactivation in the presence of water.
Type of Medium:
Online Resource
ISSN:
2052-1553
Language:
English
Publisher:
Royal Society of Chemistry (RSC)
Publication Date:
2023
Permalink