Journal of Applied Physics, AIP Publishing, Vol. 98, No. 2 ( 2005-07-15)
Abstract:
The domain structure of furnace-cooled (FC) and post-annealed (PA) Fe–xat.% Ga (x=12, 20, and 25) crystals has been investigated by magnetic force microscopy. For both FC and PA Fe–12at.% Ga, the domains were found to be well-aligned and oriented along the [100] direction. For Fe–20at.% Ga, although a preferred [100] orientation remained, a difference in morphology was found between FC and PA conditions—in the PA condition, clear dendritic domains were observed. For both FC and PA Fe–25at.% Ga, a much reduced [100] preferred domain orientation was found, the domain size was notably reduced, and dendrite formation was not observed.