Nanomaterials, MDPI AG, Vol. 11, No. 5 ( 2021-04-27), p. 1124-
Abstract:
The observation of neutrinoless double beta decay is an important issue in nuclear and particle physics. The development of organic liquid scintillators with high transparency and a high concentration of the target isotope would be very useful for neutrinoless double beta decay experiments. Therefore, we propose a liquid scintillator loaded with metal oxide nanoparticles containing the target isotope. In this work, 6-phenylhexanoic acid-modified ZrO2 nanoparticles, which contain 96Zr as the target isotope, were synthesized under sub/supercritical hydrothermal conditions. The effects of the synthesis temperature on the formation and surface modification of the nanoparticles were investigated. Performing the synthesis at 250 and 300 °C resulted in the formation of nanoparticles with smaller particle sizes and higher surface modification densities than those prepared at 350 and 400 °C. The highest modification density (3.1 ± 0.2 molecules/nm2) and Zr concentration of (0.33 ± 0.04 wt.%) were obtained at 300 °C. The surface-modified ZrO2 nanoparticles were dispersed in a toluene-based liquid scintillator. The liquid scintillator was transparent to the scintillation wavelength, and a clear scintillation peak was confirmed by X-ray-induced radioluminescence spectroscopy. In conclusion, 6-phenylhexanoic acid-modified ZrO2 nanoparticles synthesized at 300 °C are suitable for loading in liquid scintillators.
Type of Medium:
Online Resource
ISSN:
2079-4991
DOI:
10.3390/nano11051124
Language:
English
Publisher:
MDPI AG
Publication Date:
2021
detail.hit.zdb_id:
2662255-5
Permalink