Materials Science Forum, Trans Tech Publications, Ltd., Vol. 475-479 ( 2005-1), p. 577-580
Abstract:
The primary creep behavior at ambient temperature of typical h.c.p., b.c.c. and f.c.c. metals and alloys of annealed state was surveyed and the deformation mechanism of CP-Ti was discussed through transmission electron microscopy. Only h.c.p. metals and alloys demonstrated significant creep at ambient temperature. Arrays of straight screw dislocations of b=1/2 〈 2110 〉 and 〈 2110 〉 direction were observed in the crept CP-Ti.